Product Name:SUS201 Stainless Steel Round bar
Chemical Composition:
(C) :≤0.15
(Si) :≤1.00
(Mn) :5.5～7.50
(Cr) :16.0～18.0
(N) :≤0.25
(P) :≤0.060
(S) :≤0.030
(Ni) : 3.5-5.5
ASTM A666
Mechanical Property:
Tensile strength: 520mpa
Yield strength: 275mpa
Elongation: 55 to 60%
The elastic modulus of the material is 29000000 psi, which is equivalent to 203000mpa. This important factor indicates how the material responds to stress and strain. It is a measure of the stiffness of a material, and it is essential for understanding how the material behaves under different conditions. The value of the elastic modulus provides information on the amount of force required to cause deformation in the material. Therefore, it is a critical parameter in various fields such as engineering, science, and manufacturing. Understanding the elastic modulus of materials is essential for designing and constructing safe and reliable structures or products.
To meet the specified hardness requirement, the Brinell hardness value should not exceed 183n / mm² (MPA). This means that the material being tested must have a certain level of resistance against indentation or deformation under a specified amount of force. Meeting this standard is crucial for ensuring the quality and durability of a wide range of materials used in various industries. Achieving the desired level of hardness requires proper testing and analysis, and the use of appropriate techniques and tools. By meeting this requirement, materials can be deemed suitable for their intended applications and provide reliable performance over time.
Density: 280lbs / cubic inch (density: 7.93g/cm3)
Product Shows
Feature processing technology
The surface of 1D is composed of fog particles that are discontinuous in nature. This surface is achieved through a processing technique that involves hot rolling, followed by annealing shot peening, cold rolling, as well as annealing and pickling.
The color of the 2D material is a gentle shade of silvery white. The processing technique involved in its production includes hot rolling, annealing shot peening, cold rolling, and final processing steps of annealing and pickling.
The 2B surface is known for its smoothness and silvery white gloss that is superior to the 2D surface. This surface is achieved through a series of processing technologies which include hot rolling, annealing, shot peening, pickling, cold rolling, annealing, pickling, as well as quenching and tempering rolling. These processes ensure that the final product has a flawless finish with outstanding aesthetic appeal.
The surface of Ba exhibits remarkable shine and an incredibly reflective quality, comparable to the smooth surface of a mirror. The manufacturing process involves various techniques, such as hot rolling followed by annealing, shot peening, pickling and cold rolling, as well as additional annealing and pickling steps. To attain the final product, quenching and tempering rolling is required, along with rigorous surface polishing.
A desirable characteristic for a surface finish would be a smooth and shiny appearance, combined with a slightly rough texture. This can be achieved through a variety of processing techniques, such as polishing, quenching, and tempering rolling. For products with a 2D shape, or those with a 2B finish, an abrasive material with a grit size of 100-120 (as defined by JIS R6002) can be used during processing in order to achieve the desired surface quality.
Number 4 highlights the desirable qualities of having a good gloss and fine grain on the surface. The recommended processing technology for achieving these qualities is through the use of polishing, quenching, and tempering rolling. This technique is applicable for both 2D products or 2B finishes, using abrasive materials with a grit range of 150 to 180, as specified by JIS R6002 standards. By rearranging the provided information, we can ensure that the generated content remains consistent with the original text.
Silver gray HL is achieved by applying hairline stripes during the processing technology. In this process, the 2D or 2B products undergo polishing using abrasive materials of suitable particle size. This polishing creates continuous grinding lines on the surface, resulting in the desired silver gray appearance.
The mirror state of Mirro involves utilizing processing technology. In this process, the 2D or 2B products undergo grinding and polishing using abrasive materials of suitable particle size. This meticulous procedure ensures that the products achieve a stunning mirror effect.
Contact
Jamie Wang
Sales Manager
Wuxi Mingshang Steel
China
Mail:jamiewang@mstgsteel.com
Whatsapp/Mob:86 13812044786
skype:86 13812044786(Jamie Wang)
Wechat:13812044786
Hot Tags: sus 201 stainless steel round bar, China sus 201 stainless steel round bar manufacturers, suppliers, factory